Viscosity Part A cps 25°C
|
Tixotropic paste
|
|
Viscosity Part B cps 25°C
|
Tixotropic paste
|
|
Density Part A/Part B at 25°C gr/cm
3
|
1.3/1.3
|
|
Aspect Part A/Aspect Part B
|
Ivory paste/white paste
|
|
Aspect Resin Hard
|
White
|
|
GARDNER color of the resin ASTM D1544
|
NA
|
|
GARDNER color of the hardener ASTM D1544
|
NA
|
|
Mixing ratio resin + hardener in weight
|
100 + 100 = Total 200
|
|
Gel time in bulk at 25°C (100 gr resin + hardener)
|
Approximately 2h 30min
|
|
Tacky free in thin layer at 25°C; 50% relative humidity
|
Approximately 4 hours
|
|
Tacky free in thin layer at 40°C; 10% relative humidity
|
Approximately 3 hours
|
|
Hardness in Shore D (1) ASTM D 2240
|
81
|
|
Glass transition temperature Tglass (ASTM E1545) (1)
|
62 °C
|
|
Peeling test with glass fiber on marble (ASTM D3167) (1)
|
1,5 N/mm
|
|
Adhesion force on marble (ASTM D4541)(1)
|
15 Mpa
|
|
Adhesion force on glass (ASTM D4541)(1)
|
15 Mpa
|
|
Weathering test on climatic chamber Qsun, (ASTM D904), 3 years of outdoor condition, light+rain+ thermal shock
|
Passed, no detatchment of resin from the support
|
|
Yellowing test on the Xenon chamber 3 years (ISO11341)
|
Very high
|
|
Minimum reaction temperature
|
+5 °C
|
|
Minimum temperature of use after hardening
|
-25 °C
|
|
Maximum temperature of use after hardening
|
+60 °C
|
|
Working time at 25 °C (time for polishing or cutting)
|
24 hours
|